刘盼, 殷海荣, 张红林等. 高Tb<sup>3+</sup>离子含量磁光玻璃的Faraday效应及发光性能[J]. 发光学报, 2015,36(3): 293-298
LIU Pan, YIN Hai-rong, ZHANG Hong-lin etc. Faraday Effect and Luminescence Properties of Magneto-optical Glasses With High Tb<sup>3+</sup> Content[J]. Chinese Journal of Luminescence, 2015,36(3): 293-298
刘盼, 殷海荣, 张红林等. 高Tb<sup>3+</sup>离子含量磁光玻璃的Faraday效应及发光性能[J]. 发光学报, 2015,36(3): 293-298 DOI: 10.3788/fgxb20153603.0293.
LIU Pan, YIN Hai-rong, ZHANG Hong-lin etc. Faraday Effect and Luminescence Properties of Magneto-optical Glasses With High Tb<sup>3+</sup> Content[J]. Chinese Journal of Luminescence, 2015,36(3): 293-298 DOI: 10.3788/fgxb20153603.0293.
采用高温熔融法制备了高Tb
3+
离子含量的GeO
2
-B
2
O
3
-SiO
2
系统磁光玻璃
测试了其Verdet常数和发光性能
探究了玻璃的Faraday效应、发光性能及光学碱度。研究结果表明:Verdet常数和光学碱度均随着Tb
2
O
3
含量的增加而线性增大
当Tb
2
O
3
摩尔分数为70%时
Verdet常数达到-5 000 minT
-1
cm
-1
(632.8 nm)
所有磁光玻璃样品随Tb
2
O
3
含量变化均发出明亮的黄绿光。由于浓度猝灭效应
高Tb
2
O
3
含量缩短了Tb
3+
离子间距
增强了交叉弛豫效应
降低了发光强度和荧光寿命。
GeO
2
-B
2
O
3
-SiO
2
magneto-optical glasses with high Tb
3+
content were prepared by high temperature melting technique. The effect of Tb
3+
content on the Faraday effect
luminescent properties and optical basicity was studied. The results show that Verdet constant and optical basicity increase with the increasing of Tb
2
O
3
content. All samples emit bright greenish-yellow luminescence
and the glass has a higher Verdet constant of -5 000 minT
-1
cm
-1
at 632.8 nm when the mole fraction of Tb
2
O
3
is 70%. The distances among Tb
3+
ions become shorter with the increasing of Tb
2
O
3
content due to the concentration quenching effect
therefore
the cross-relaxation effect is enhanced
and the effective luminous intensity and lifetime decrease.
磁光玻璃光学碱度Tb3+光致发光
magneto-optical glassoptical basicityTb3+photoluminescence
Ouedraogo K, Topsu S, Gayhmouni J, et al. Accurate ellipsometric magnetic-field sensor used to align the watt balance magnetic circuit of the French National Metrology Institute [J]. Sens. Actuat. A, 2012, 175:9-14.
Akamatsu H, Fujita K, Nakatsuka Y, et al. Magneto-optical properties of Eu2+-containing aluminoborosilicate glasses with ferromagnetic interactions [J]. Opt. Mater., 2013, 35(11):1997-2000.
Tsutsumi M. Optical isolator-modulator in a microstrip line on yttrium iron garnet single crystal [J]. IEICE. T. Electron., 2001, 84(3):325-330.
Burzo E, Ardelean I, Ursu I, et al. Magnetic properties of xEu2O3(1-x) glasses [J]. Mater. Lett., 1996, 26:103-105.
Culea E, Pop A, Cosma I, et al. Magnetic behaviour of xGd2O3(1-x) Na2O2B2O3 glasses [J]. J. Magn. Magn. Mater., 1996, 157:163-164.
Culea E, Ristoiu T, Bratu I, et al. Magnetic and structural behaviour of some borate glasses containing holmium ions [J]. Mater. Sci. Eng. B, 1999, 57:259-261.
Culea E, Ristoiu T, Bratu I, et al. Structural and magnetic behavior of some borate glasses containing europium ions [J]. Mater. Sci. Eng. B, 2000, 75:82-84.
Malakhovskii A V, Edelman I S, Radzyner Y, et al. Magnetic and magneto-optical properties of oxide glasses containing Pr3+, Dy3+ and Nd3+ ions [J]. J. Magn. Magn. Mater., 2003, 263(2):161-172.
Garaje S N, Apte S K, Kumar G, et al. Ferric oxide quantum dots in stable phosphate glass system and their magneto-optical study [J]. Mater. Res. Bull., 2013, 48(2):901-906.
Alers P B. Faraday effect in cerium phosphate glasses at low temperatures [J]. Phys. Rev., 1959, 116(6):1483.
Rubinstein C, Berger S, Van Uitert L, et al. Faraday rotation of rare-earth (Ⅲ) borate glasses [J]. J. Appl. Phys., 2004, 35(8):2338-2340.
Li C Y, Wu Y M, Cao L M, et al. Magneto-optical modulation method for measuring glass internal stress [J]. Opt. Precision Eng.(光学 精密工程), 2014, 22(1):58-62 (in Chinese).
Petrovskii G, Edelman I, Zarubina T, et al. Faraday effect and spectral properties of high-concentrated rare earth oxide glasses in visible and near UV region [J]. J. Non-Cryst. Solids, 1991, 130(1):35-40.
Qiu J, Higuchi H, Kawamoto Y, et al. Faraday effect of GaS3/2-GeS2-LaS3/2-based glasses containing various rare-earth ions [J]. J. Appl. Phys., 1996, 80(9):5297-5300.
Qiu J, Kawamoto Y, Hirao K. Faraday effect of ZrF4-BaF2-LnF3 glasses (Ln=La, Ce, Pr, Tb and Dy) [J]. Jpn. J. Appl. Phys., 1997, 36:1091-1093.
Hayakawa T, Nogami M, Nishi N, et al. Faraday rotation effect of highly Tb2O3/Dy2O3-concentrated B2O3-Ga2O3-SiO2-P2O5 glasses [J]. Chem. Mater., 2002, 14(8):3223-3225.
Tanaka K, Fujita K, Soga N, et al. Faraday effect of sodium borate glasses containing divalent europium ions [J]. J. Appl. Phys., 1997, 82(2):840-844.
Zu C, Chen J, Zhao H, et al. Effect of cerium on luminescence and irradiation resistance of Tb3+ doped silicate glasses [J]. J. Alloys Compd., 2009, 479(1):294-298.
Witkowska A, Padlyak B, Rybicki J, An EXAFS study of the local structure of rare-earth luminescence centres in the 3CaO-Ga2O3-3GeO2 glass [J]. Opt. Mater., 2008, 30:699-702.
Doweidar H. Considerations on the structure and physical properties of B2O3-SiO2 and GeO2-SiO2 glasses [J]. J. Non-Cryst. Solids, 2011, 357(7):1665-1670.
Rejisha S, Santha N. Structural investigations on 20MO-xBi2O3-(80-x)B2O3 (M= Ca, Sr and Ba; x= 15 and 55) glasses [J]. J. Non-Cryst. Solids, 2011, 357(22):3813-3821.
Zhao S, Xin F, Xu S, et al. Luminescence properties and energy transfer of Eu/Tb ions codoped aluminoborosilicate glasses [J]. J. Non-Cryst. Solids, 2011, 357(11):2424-2427.
Pershan P. Magneto-optical effects [J]. J. Appl. Phys., 2004, 38:1482-1490.
Duffy J. Redox equilibria in glass [J]. J. Non-Cryst. Solids, 1996, 196:45-50.
Komatsu T, Ito N, Honma T, et al. Electronic polarizability and its temperature dependence of Bi2O3-B2O3 glasses [J]. J. Non-Cryst. Solids, 2010, 356(49):2310-2314.
Pal Singh G, Kaur P, Kaur S, et al. Investigation of structural, physical and optical properties of CeO2-Bi2O3-B2O3 glasses [J]. Physica B, 2012, 407(21):4168-4172.
Dimitrov V, Sakka S. Electronic oxide polarizability and optical basicity of simple oxides [J]. J. Appl. Phys., 1996, 79(3):1736-1740.
Zhao X, Wang X, Lin H, et al. Electronic polarizability and optical basicity of lanthanide oxides [J]. Physica B, 2007, 392(1):132-136.
Zhang Q, Chen G, Xu Y, et al. Abnormal upconversion luminescence from Yb3+ doped and Tb3+/Yb3+ codoped high silica glasses induced by intrinsic optical bistability [J]. Chem. Appl. Phys. B, 2010, 98(3):261-265.
Gu L S, Shi N, Zhang L, et al. Synthesis and luminescent properties of Tb/Eu co-doped zinc borophosphate glasses for white light generation [J]. Chin. J. Lumin.(发光学报), 2014, 35(8):897-904 (in Chinese).
Zhang L, Peng M, Dong G, et al. An investigation of the optical properties of Tb3+-doped phosphate glasses for green fiber laser [J]. Opt. Mater., 2012, 34(7):1202-1207.
Jiao H, Liao F, Tian S, et al. Influence of rare earth Sc and La to the luminescent properties of FED blue phosphor Y2SiO5:Ce [J]. J. Electrochem. Soc., 2004, 151(7):39-42.
He D, Yu C, Cheng J, et al. Effect of Tb3+ concentration and sensitization of Ce3+ on luminescence properties of terbium doped phosphate scintillating glass [J]. J. Alloys Compd., 2011, 509(5):1906-1909.
Dejneka M, Snitzer E, Riman R. Spectroscopic characterization of Eu3+-doped inorganic and alkoxide sol-gel derived fluorozirconate glass and zirconium fluoride gels [J]. J. Non-Cryst. Solids, 1996, 202(1):23-34.
Williams D K, Bihari B, Tissue B M, et al. Preparation and fluorescence spectroscopy of bulk monoclinic Eu3+:Y2O3 and comparison to Eu3+:Y2O3 nanocrystals [J]. J. Phys. Chem. B, 1998, 102:916-920.
Campbell J, Suratwala T. Nd-doped phosphate glasses for high-energy/high-peak-power lasers [J]. J. Non-Cryst. Solids,2000, 263:318-341.
Tsuboi T. Optical properties of Ce3+/Tb3+-codoped borosilicate glass [J]. Eur. Phys. J.Appl. Phys., 2004, 26(2): 95-101.
Ratnakaram Y, Tirupathi Naidu D, Chakradhar R. Absorption and emission properties of Nd3+ in lithium cesium mixed alkali borate glasses [J]. Solid State Commun., 2005, 136(1):45-50.
Meng X G, Qiu J R, Peng M Y, et al. Near infrared broadband emission of bismuth-doped aluminophosphate glass [J]. Opt. Express, 2005, 406(5):1628-1634.
Rajyasree C, Vinaya Teja P M, Murthy K, et al. Optical and other spectroscopic studies of lead, zinc bismuth borate glasses doped with CuO [J]. Physica B, 2011, 406(23):4366-4372.
0
浏览量
31
下载量
1
CSCD
关联资源
相关文章
相关作者
相关机构