李开宇, 王如志, 曲铭浩, 张影, 严辉. Pr<sup>3+</sup>,Yb<sup>3+</sup>共掺YPO<sub>4</sub>下转换材料的制备及其转光效率[J]. 发光学报, 2012,(5): 486-491
LI Kai-yu, WANG Ru-zhi, QU Ming-hao, ZHANG Ying, YAN Hui. Downconversion Materials Preparation and The Research of Conversion Efficiency in Pr<sup>3+</sup>, Yb<sup>3+</sup> Co-doped YPO<sub>4</sub>[J]. Chinese Journal of Luminescence, 2012,(5): 486-491
李开宇, 王如志, 曲铭浩, 张影, 严辉. Pr<sup>3+</sup>,Yb<sup>3+</sup>共掺YPO<sub>4</sub>下转换材料的制备及其转光效率[J]. 发光学报, 2012,(5): 486-491 DOI: 10.3788/fgxb20123305.0486.
LI Kai-yu, WANG Ru-zhi, QU Ming-hao, ZHANG Ying, YAN Hui. Downconversion Materials Preparation and The Research of Conversion Efficiency in Pr<sup>3+</sup>, Yb<sup>3+</sup> Co-doped YPO<sub>4</sub>[J]. Chinese Journal of Luminescence, 2012,(5): 486-491 DOI: 10.3788/fgxb20123305.0486.
采用固相反应法制备了Pr
3+
Yb
3+
共掺杂的YPO
4
下转换发光粉体
并在450 nm光激发条件下
研究了Yb
3+
不同摩尔分数(0%
1%
2%
4%
20%
30%)对转光效率的影响。结果表明:不同Yb
3+
浓度的样品
其荧光峰强度不同
这可能是由于Pr
3+
-Yb
3+
之间Yb
3+
浓度不同存在能量传递效率差异的原因。研究也发现了样品的下转换发光
其能量传递过程为:Pr
3+
:
3
P
0
Yb
3+
:
2
F
5/2
+
2
F
5/2
。荧光光谱测试结果表明
Yb
3+
的最佳掺杂摩尔分数为2%。Pr
3+
Yb
3+
共掺杂的YPO
4
材料在提高太阳能电池光电转换效率方面具有潜在的应用。
Pr
3+
Yb
3+
co-doped YPO
4
downconversion phosphor powders were prepared by solid state reaction. When excitation at 450 nm
the effects of different Yb
3+
mole fractions (0%
1%
2%
4%
20%
30%) on the conversion efficiency are studied. Results shows that because of the difference of energy transfer efficiency between Pr
3+
and Yb
3+
the samples with various Yb
3+
doping concentrations have different fluorescence intensity. It is also found that the energy transfer process of the downconversion luminescence in samples is Pr
3+
:
3
P
0
Yb
3+
:
2
F
5/2
+
2
F
5/2
. From photoluminescence spectra measurement
the optimal doping mole fraction of Yb
3+
is 2%. The results indicate that Pr
3+
Yb
3+
co-doped YPO
4
downconversion phosphor is a kind of potential material which may be used to improve the solar cell efficency.
下转换稀土离子YPO4太阳能电池
downconversionrare earthYPO4solar cells
Tuerxun Aidilibike, Deng Kaimo, Chen Yonghu, et al. Highly efficient near-infrared quantum cutting in LaF3:Ho3+, Yb3+ for solar cells [J]. Chin. J. Lumin.(发光学报), 2011, 32(11):1133-1138 (in Chinese).[2] Trupke T, Green M A, Wurfel P. Improving solar cell efficiencies by down-conversion of high-energy photons [J]. J. Appl. Phys., 2002, 92(3):1668-1674.[3] Serrano D, Braud A, Doualan J L, et al. Ytterbium sensitization in KY3F10:Pr3+, Yb3+ for silicon solar cells efficiency enhancement [J]. Optical Materials, 2011, 33(7):1028-1031.[4] Richards B S. Luminescent layers for enhanced silicon solar cell performance:Down-conversion [J]. Solar Energy Materials and Solar Cells, 2006, 90(9):1189-1207.[5] van Wijngaarden J T, Scheidelaar S, Vlugt T J H, et al. Energy transfer mechanism for downconversion in the (Pr3+, Yb3+) couple [J]. Physical Review B, 2010, 81(15):155112-1-6.[6] Liu Chunxu, Wang Pengcheng, Luo Yongshi, et al. Tb3+-Er3+ couples as spectral converters in NaYF4 for GaAs solar cells [J]. Chin. J. Lumin.(发光学报), 2011, 32(11):1120-1125 (in Chinese).[7] Aarts L, van der Ende B, Reid M F, et al. Downconversion for solar cells in YF3:Pr3+, Yb3+ [J]. Spectroscopy Letters, 2010, 43(5):373-381.[8] Chen X B, Yang J G, Zhang C L, et al. Infrared quantum-cutting analysis of Er0.3Gd0.7VO4 crystal for solar cell application [J]. Acta Physica Sinica (物理学报), 2010, 59(11):8191-8199 (in Chinese).[9] Chen X P, Huang X Y, Zhang Q Y. Concentration-dependent near-infrared quantum cutting in NaYF4:Pr3+,Yb3+ phosphor [J]. J. Appl. Phys., 2009, 106(6):063518-1-3.[10] Yang G M, Zhou S M, Lin H, et al. Down-conversion near infrared emission in Pr3+,Yb3+ co-doped Y2O3 transparent ceramics [J]. Physica B: Condensed Matter, 2011, 406(19):3588-3591.[11] Vergeer P, Vlugt T J H, Kox M H F, et al. Quantum cutting by cooperative energy transfer in YbxY1-xPO4:Tb3+ [J]. Physical Review B, 2005, 71(1):014119-1-11.[12] Zhang Q Y, Yang C H, Pan Y X. Cooperative quantum cutting in one-dimensional (YbxGd1-x)Al3(BO3)4:Tb3+ nanorods [J]. Appl. Phys. Lett., 2007, 90(2):021107-1-3.[13] Zhang Q Y, Yang C H, Jiang Z H, et al. Concentration-dependent near-infrared quantum cutting in GdBO3:Tb3+, Yb3+ nanophosphors [J]. Appl. Phys. Lett., 2007, 90(6):061914-1-3.[14] Zhang Q Y, Yang C H, Jiang Z H. Cooperative downconversion in GdAl3(BO3)4:RE3+, Yb3+(RE=Pr, Tb, and Tm) [J]. Applied Physics Letters, 2007, 91(5):051903-1-3.[15] Xie L C, Wang Y H, Zhang H J. Near-infrared quantum cutting in YPO4:Yb3+, Tm3+ via cooperative energy transfer [J]. Appl. Phys. Lett., 2009, 94(6):061905-1-3.[16] Chen D Q, Wang Y S, Yu Y L, et al. Quantum cutting downconversion by cooperative energy transfer from Ce3+ to Yb3+ in borate glasses [J]. J. Appl. Phys., 2008, 104(11):8989-8994.[17] Liu X F, Qiao Y B, Dong G P, et al. Cooperative downconversion in Yb3+-RE3+(RE=Tm or Pr) codoped lanthanum borogermanate glasses [J]. Optics Letters, 2008, 33(23):2858-2860.[18] Ye S, Zhu B, Luo J, et al. Enhanced cooperative quantum cutting in Tm3+-Yb3+ codoped glass ceramics containing LaF3 nanocrystals [J]. Optics Express, 2008, 16(12):8989-8994.[19] Ye S, Zhu B, Chen J X, et al. Infrared quantum cutting in Tb3+, Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals [J]. Appl. Phys. Lett., 2008, 92(14):141112-1-3.[20] Wang Y S, Chen D Q, Yu Y L, et al. Near-infrared quantum cutting in transparent nanostructured glass ceramics [J]. Optics Letters, 2008, 33(16):1884-1886.[21] Chen D Q, Yu Y L, Wang Y S, et al. Cooperative energy transfer up-conversion and quantum cutting down-conversion in Yb3+:TbF3 nanocrystals embedded glass ceramics [J]. J. Phys. Chem. C, 2009, 113(16):6406-6410.[22] Lin H, Chen D Q, Yu Y L, et al. Near-infrared quantum cutting in Ho3+/Yb3+ codoped nanostructured glass ceramic [J]. Optics Letters, 2011, 36(6):876-878.[23] Chen D Q, Yu Y L, Lin H, et al. Ultraviolet-blue to near-infrared downconversion of Nd3+-Yb3+ couple [J]. Optics Letters, 2010, 35(2):220-222.[24] Lin H, Zhou S M, Teng H, et al. Near infrared quantum cutting in heavy Yb doped Ce0.03Yb3xY(2.97-3x)Al5O12 transparent ceramics for crystalline silicon solar cells [J]. J. Appl. Phys., 2010, 107(4):876-878.[25] Lin H, Zhou S M, Hou X R, et al. Down-conversion from blue to near infrared in Tm3+-Yb3+ codoped Y2O3 transparent ceramics [J]. IEEE Photonics Technology Letters, 2010, 22(12):866-868.[26] Huang X Y, Zhang Q Y. Efficient near-infrared down conversion in Zn2SiO4:Tb3+, Yb3+ thin-films [J]. J. Appl. Phys., 2009, 105(5):053521-1-4.[27] de Sousa P C, Serra O A. Reverse microemulsion synthesis, structure, and luminescence of nanosized REPO4:Ln3+(RE=La, Y, Gd, or Yb, and Ln=Eu, Tm, or Er) [J]. J. Phys. Chem. C, 2011, 115(3):636-646.[28] Capelletti R, Baraldi A, Buffagni E, et al. Optical spectroscopy of YPO4 single crystals doped with Ho3+ [J]. Spectroscopy Letters, 2010, 43(5):382-388.[29] de Sousa P C, Serra O A. Red, green, and blue lanthanum phosphate phosphors obtained via surfactant-control led hydrothermal synthesis [J]. J. Lumin., 2009, 129(12):1664-1668.[30] Moine B, Hachani S, Ferid M. Energy transfer between Sm3+ and Er3+ in orthophosphate YPO4 [J]. J. Lumin., 2011, 131(10):2110-2115.[31] Lian R, Yin M, Zhang W P, et al. Chemical preparation, structure analysis and spectrum characteristics of YPO4:Pr3+ nanocrystal [J]. Chin. J. Lumin.(发光学报), 1999, 20(2):102-105 (in Chinese).[32] Lecointre A, Bessiere A, Bos A J J, et al. Designing a red persistent luminescence phosphor:The example of YPO4:Pr3+, Ln3+ (Ln=Nd, Er, Ho, Dy) [J]. J. Phys. Chem. C, 2011, 115(10):4217-4227.[33] Yuan J L, Zeng X Y, Zhao J T, et al. Energy transfer mechanisms in Tb3+, Yb3+ codoped Y2O3 downconversion phosphor [J]. J. Phys. D: Appl. Phys., 2008, 41(10):105406-1-6.[34] Chen H T, Yin M, Lian R, et al. Luminescence dependence upon concentration and temperature in YPO4:Pr3+ [J]. Spectroscopy and Spectral Analysis (光谱学与光谱分析), 2001, 21(2):151-154 (in Chinese).