齐敬强, 邓振波, 刘梦林等. PEG掺杂对钙钛矿太阳能电池的影响[J]. 发光学报, 2017,38(4): 457-462
QI Jing-qiang, DENG Zhen-bo, LIU Meng-lin etc. Influence of PEG Doping on The Perovskite Solar Cells[J]. Chinese Journal of Luminescence, 2017,38(4): 457-462
齐敬强, 邓振波, 刘梦林等. PEG掺杂对钙钛矿太阳能电池的影响[J]. 发光学报, 2017,38(4): 457-462 DOI: 10.3788/fgxb20173804.0457.
QI Jing-qiang, DENG Zhen-bo, LIU Meng-lin etc. Influence of PEG Doping on The Perovskite Solar Cells[J]. Chinese Journal of Luminescence, 2017,38(4): 457-462 DOI: 10.3788/fgxb20173804.0457.
为了提高钙钛矿太阳能电池的能量转化效率'减小回滞现象'研究了聚乙二醇(PEG)掺杂钙钛矿太阳能电池阳极修饰层PEDOT:PSS对器件性能的影响。通过电容-电压(
C-V
)测试分析了PEDOT:PSS修饰层和钙钛矿层之间的界面电荷积累情况'通过电流密度-时间(
J-T
)瞬态光电流的测量研究了修饰层和钙钛矿层之间缺陷态情况。结果表明'PEG掺杂阳极修饰层提高了器件的短路电流(
J
sc
)、开路电压(
V
oc
)和填充因子(FF)'光电转化效率从7.5%提高到10.0%'光电转化效率提高了33%'经过掺杂后的器件回滞现象明显减弱。这种通过PEG掺杂PEDOT:PSS的方法能够减少器件界面处的电荷积累和缺陷态'从而减小器件的回滞现象'提高器件的能量转化效率。
Polyethylene glycol (PEG) was doped into the PEDOT:PSS layer of CH
3
NH
3
PbI
x
Cl
3-
x
perovskite solar cells to improve the power conversion efficiency (PCE) and reduce the hysteresis of the device. The capacitance-voltage (
C-V
) and the current density-time (
J-T
) transient measurements were used to study the charge accumulation and defects between the buffer layer and the active layer. The results show that the short circuit current (
J
sc
)
the open circuit voltage (
V
oc
)
the fill factor (FF)
and the power conversion efficiency (PCE) of the device with PEG are improved. The PCE of the device with PEG reaches 10.0% which is 33% higher than that of the control device and the hysteresis of
J-V
curve is also reduced with the introduction of PEG. PEG can improve the device properties by reducing the charge accumulation and decreasing the defects which is beneficial to electron collection and reducing hysteresis.
钙钛矿掺杂回滞电荷积累聚乙二醇(PEG)
perovskitedopinghysteresischarge accumulationpolyethylene glycol (PEG)
SEO J, PARK S, KIM Y C, et al.. Benefits of very thin PCBM and LiF layers for solution-processed p-i-n perovskite solar cells[J]. Energy Environ. Sci., 2014, 7(8):2642-2646.
KOJIMA A, TESHIMA K, SHIRAI Y, et al.. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells[J]. J. Am. Chem. Soc., 2009, 131(17):6050-6051.
YANG W S, NOH J H, JEON N J, et al.. High-performance photovoltaic perovskite layers fabricated through intramolecular exchange[J]. Science, 2015, 348(6240):1234-1237.
XI J, WU Z X, DONG H, et al.. Controlled thickness and morphology for highly efficient inverted planar heterojunction perovskite solar cells[J]. Nanoscale, 2015, 7(24):10699-10707.
CHIANG C H, TSENG Z L, WU C G. Planar heterojunction perovskite/PC71BM solar cells with enhanced open-circuit voltage via a (2/1)-step spin-coating process[J]. J. Mater. Chem. A, 2014, 2(38):15897-15903.
XIAO Z G, BI C, SHAO Y C, et al.. Efficient, high yield perovskite photovoltaic devices grown by interdiffusion of solution-processed precursor stacking layers[J]. Energy Environ. Sci., 2014, 7(8):2619-2623.
KIM H B, CHOI H, JEONG J, et al.. Mixed solvents for the optimization of morphology in solution-processed, inverted-type perovskite/fullerene hybrid solar cells[J]. Nanoscale, 2014, 6(12):6679-6683.
CHEN Q, ZHOU H P, HONG Z R, et al.. Planar heterojunction perovskite solar cells via vapor-assisted solution process[J]. J. Am. Chem. Soc., 2014, 136(2):622-625.
ZHAO Y X, ZHU K. Three-step sequential solution deposition of PbI2-free CH3NH3PbIM3 perovskite[J]. J. Mater. Chem. A, 2015, 3(17):9086-9091.
ZHANG H, MAO J, HE H X, et al.. A smooth CH3NH3PbI3 film via a new approach for forming the PbI2 nanostructure together with strategically high CH3NH3I concentration for high efficient planar-heterojunction solar cells[J]. Adv. Energy Mater., 2015, 5(23):1501354.
DU Y Y, CAI H K, NI J, et al.. Air-processed, efficient CH3NH3PbI3-xClx perovskite solar cells with organic polymer PTB7 as a hole-transport layer[J]. RSC Adv., 2015, 5(82):66981-66987.
LIU Y, BAG M, RENNA L A, et al.. Understanding interface engineering for high-performance fullerene/perovskite planar heterojunction solar cells[J]. Adv. Energy Mater., 2016, 6(2):1501606.
YOU J B, HONG Z R, YANG Y, et al.. Low-temperature solution-processed perovskite solar cells with high efficiency and flexibility[J]. ACS Nano, 2014, 8(2):1674-1680.
ZHAO Y X, ZHU K. CH3NH3Cl-assisted one-step solution growth of CH3NH3PbI3:structure, charge-carrier dynamics, and photovoltaic properties of perovskite solar cells[J]. J. Phys. Chem. C, 2014, 118(18):9412-9418.
JENG J Y, CHIANG Y F, LEE M H, et al.. CH3NH3PbI3 perovskite/fullerene planar-heterojunction hybrid solar cells[J]. Adv. Mater., 2013, 25(27):3727-3732.
WANG K, LIU C, YI C, et al.. Efficient perovskite hybrid solar cells via ionomer interfacial engineering[J]. Adv. Funct. Mater., 2015, 25(44):6875-6884.
HUANG X, WANG K, YI C, et al.. Efficient perovskite hybrid solar cells by highly electrical conductive PEDOT:PSS hole transport layer[J]. Adv. Energy Mater., 2016, 6(3):1501773.
LANG U, MLLER E, NAUJOKS N, et al.. Microscopical investigations of PEDOT:PSS thin films[J]. Adv. Funct. Mater., 2009, 19(8):1215-1220.
NA S I, WANG G, KIM S S, et al.. Evolution of nanomorphology and anisotropic conductivity in solvent-modified PEDOT:PSS films for polymeric anodes of polymer solar cells[J]. J. Mater. Chem., 2009, 19(47):9045-9053.
MCNEILL C R, HWANG I, GREENHAM N C. Photocurrent transients in all-polymer solar cells:trapping and detrapping effects[J]. J. Appl. Phys., 2009, 106(2):024507.
CHO S, KIM K D, HEO J, et al.. Role of additional PCBM layer between ZnO and photoactive layers in inverted bulk-heterojunction solar cells[J]. Sci. Rep., 2014, 4:4306.
CHEN B B, QIAO X F, LIU C M, et al.. Effects of bulk and interfacial charge accumulation on fill factor in organic solar cells[J]. Appl. Phys. Lett., 2013, 102(19):193302.
ZANG H D, HSIAO Y C, HU B. Surface-charge accumulation effects on open-circuit voltage in organic solar cells based on photoinduced impedance analysis[J]. Phys. Chem. Chem. Phys., 2014, 16(10):4971-4976.
0
浏览量
56
下载量
0
CSCD
关联资源
相关文章
相关作者
相关机构