谢丽娟, 蔡建亮, 张蕤, 邹阳, 孟建新. 溶剂热法制备的纳米BaSnO<sub>3</sub>及其近红外发光[J]. 发光学报, 2013,(1): 18-23
XIE Li-juan, CAI Jian-liang, ZHANG Rui, ZOU Yang, MENG Jian-xin. Solvothermal Preparetion and Near-infrared Fluorescence of BaSnO<sub>3</sub> Nanoparticles[J]. Chinese Journal of Luminescence, 2013,(1): 18-23
谢丽娟, 蔡建亮, 张蕤, 邹阳, 孟建新. 溶剂热法制备的纳米BaSnO<sub>3</sub>及其近红外发光[J]. 发光学报, 2013,(1): 18-23 DOI: 10.3788/fgxb20133401.0018.
XIE Li-juan, CAI Jian-liang, ZHANG Rui, ZOU Yang, MENG Jian-xin. Solvothermal Preparetion and Near-infrared Fluorescence of BaSnO<sub>3</sub> Nanoparticles[J]. Chinese Journal of Luminescence, 2013,(1): 18-23 DOI: 10.3788/fgxb20133401.0018.
用溶剂热法制备了BaSn(OH)
6
前驱体
经煅烧后
得到BaSnO
3
纳米粉末。用XRD、TEM、纳米粒度仪、紫外-可见-近红外分光光度计、光纤光谱仪等对样品的结构、形貌和性能进行了表征。BaSnO
3
纳米粒子为粒径约为30~50nm的球形颗粒
具有良好的分散性
也具有很好的近红外发光性能
其最大激发和发射波长分别位于385nm和895nm。与高温固相法得到的样品相比
该方法所得纳米BaSnO
3
样品的近红外发光强度提高近10倍
样品结晶程度的提高和缺陷的减少可能是样品近红外发光强度提高的主要原因。
BaSnO
3
nano-phosphors were prepared by solvothermal method using glycol-water mixed solution as a solvent
followed by calcinations at different temperature. The as-synthesized samples were characterized by X-ray diffraction (XRD)
transmission electron microscopy (TEM)
the nano-particle size analyzer
UV-Vis-NIR spectrophotometer
excitation and emission spectra. The nano-powders are sphere with sizes of 30~50 nm. Good dispersity can be achieved even after the sample was calcined. Efficient near-infrared fluorescence with emission peak of 895 nm was observed under the excitation of 385 nm. Comparing with the sample prepared by solid state reaction
the emission intensities increase about ten folds. The degree of crystallization is found to be the main fact of the near-infrared fluorescence of BaSnO
3
nanoparticles.
溶剂热法近红外发光纳米BaSnO3
solvothermalnear-infraredBaSnO3 nano-powders
Weissleder R, Ntziachristos V. Shedding light onto live molecular targets [J]. Nat. Med., 2003, 9(1):123-128.
Intes X, Ripoll J, Chen Y, et al. In vivo continuous-wave optical breast imaging enhanced with Indocyanine [J]. Green Med. Phys., 2003, 30(6):1039-1047.
Imbert D, Cabtuel M, Bunzli J C, et al. Extending lifetimes of lanthanide-based near-infrared emitters (Nd, Yb) in the millisecond range through Cr(III) sensitization in discrete bimetallic edifices [J]. J. Am. Chem. Soc., 2003, 125(51):15698-15699.
Wolcott A, Gerion D, Visconte M, et al. Silica-coated CdTe quantum dots functionalized with thiols for bioconjugation to IgG proteins [J]. J. Phys. Chem. B, 2006, 110(11):5779-5789.
Feng L Y, Kong X G. Preparation and characterization of fluorescence CdSe-liposome compound [J]. Chin. J. Lumin.(发光学报), 2007, 28(3):417-420 (in Chinese).
Feng B, Teng F, Tang A W, et al. Application of aminophenol-stabilized CdSe nanocrystals as a fluorescent label for lysozyme [J]. Chin. J. Lumin.(发光学报), 2007, 28(3):421-424 (in Chinese).
Qian H F, Dong C Q, Peng J L, et al. High-quality and water-soluble near-infrared photoluminescent CdHgTe/CdS quantum dots prepared by adjusting size and composition [J]. J. Phys. Chem. C, 2007, 111(45):16852-16857.
Bailey R E, Nie S M. Alloyed semiconductor quantum dots: Tuning the optical properties without changing the particle size [J]. J. Am. Chem. Soc., 2003, 125(23):7100-7106.
Derfus A M, Chan W C W. Probing the cytotoxicity of semiconductor quantum dots [J]. Nano Lett., 2004, 4(l):11-18.
Buse G, Preda E, Stef M, et al. Influence of Yb3+ ions on the optical properties of double-doped Er,Yb:CaF2 crystals [J]. Physica Scripta, 2011, 83(2):025604.
Sharma Y K, Surana S S L, Singh R K. Spectral studies of erbium doped soda lime silicate glasse in visible and near infrared regions [J]. Opt. Mater., 2007, 29(6):598-604.
Mizoguchi H, Woodward P W, Park C, et al. Strong near-infrared luminescence in BaSnO3 [J]. J. Am. Chem. Soc., 2004, 126(31):9796-9800.
Sano H, Herber R H. On the mssbauer parameters of bariumstannate [J]. Inorg. Nucl. Chem., 1968, 30(2):409-413.
Wagner G, Binder H. Untersuchung der binaren systeme BaO-SnO2 und BaO-PbO2.I. phasenanalysen [J]. Z. Anorg. Allg. Chem., 1958, 297:328-346.
Udawatte C P, Yoshimura M. Preparation of well-crystallized BaSnO3 powders under hydrothermal conditions [J]. Mater. Lett., 2001, 47(1/2):7-10.
Lu W S, Schmidt H. Hydrothermal synthesis of nanocrystalline BaSnO3 using a SnO2·xH2O sol [J]. J. Eur. Ceram. Soc., 2005, 25(6):919-925.
Lu W S, Schmidt H. Synthesis of tin oxide hydrate (SnO2·xH2O) gel and its effects on the hydrothermal preparation of BaSnO3 powders [J]. Adv. Powder Technol., 2008, 19(1):1-12.
Lu W S, Schmidt H. Lyothermal synthesis of nanocrystalline BaSnO3 powders [J]. Ceram. Inter., 2008, 34(3):645-649.
de Boer W D A M, Timmerman D, Dohnalova K, et al. Red spectral shift and enhanced quantum efficiency in phonon-free photoluminescence from silicon nanocrystals [J]. Nat. Nanotechnol., 2010, 5(12):878-884.
0
浏览量
31
下载量
1
CSCD
关联资源
相关文章
相关作者
相关机构