- 石英衬底上Au缓冲层对ZnO薄膜微结构的影响
- Effect of Au Buffer Layer on the Structure of ZnO Films Grown on Quartz Substrate
- 发光学报 2010年31卷第2期页码：219-222
- 作者机构：
  
  电子科技大学电子薄膜与集成器件国家重点实验室,四川成都,610054
- 作者简介：
- 基金信息：
  
  国家自然科学基金(50802012)资助项目()
- DOI：
  中图分类号： O472.3;O482.3
- 收稿日期：2009-11-02，
  
  修回日期：2010-01-09，
  
  纸质出版日期：2010
- 稿件说明：
移动端阅览
李宁, 陈金菊, 邓宏. 石英衬底上Au缓冲层对ZnO薄膜微结构的影响[J]. 发光学报, 2010,31(2): 219-222

LI Ning, CHEN Jin-ju, DENG Hong. Effect of Au Buffer Layer on the Structure of ZnO Films Grown on Quartz Substrate[J]. Chinese Journal of Luminescence, 2010,31(2): 219-222
李宁, 陈金菊, 邓宏. 石英衬底上Au缓冲层对ZnO薄膜微结构的影响[J]. 发光学报, 2010,31(2): 219-222 DOI：

LI Ning, CHEN Jin-ju, DENG Hong. Effect of Au Buffer Layer on the Structure of ZnO Films Grown on Quartz Substrate[J]. Chinese Journal of Luminescence, 2010,31(2): 219-222 DOI：

摘要

采用单源化学气相沉积(SSCVD)法，在石英衬底上以Au为缓冲层，Zn

4

(OH)

2

(O

2

CCH

3

)

6

2H

2

O为固相源制备ZnO薄膜。SEM和XRD测试ZnO薄膜的微结构，结果表明：相对于SiO

2

衬底上生长的ZnO薄膜，Au/SiO

2

衬底上生长的ZnO薄膜具有较好的结晶质量和表面平整度；对制备ZnO薄膜的衬底温度进行了工艺优化，结果表明：500℃时制备的ZnO薄膜颗粒大小均匀，结晶质量较好；通过荧光光谱仪对Au/SiO

2

衬底上的ZnO薄膜进行光致发光(PL)谱测试，ZnO薄膜在400nm出现紫光发射峰，而没有出现与缺陷相关的深能级发射峰，表明ZnO薄膜具有较好的结晶质量。

Abstract

Taking [Zn

4

(OH)

2

(O

2

CCH

3

)

6

2H

2

O] as solid sources

ZnO thin films were deposited on quartz and gold-plated quartz substrates by SSCVD technique at normal pressure. The structure and morpho-logy of the samples was characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD)

respectively

while the optical properties were estimated by photoluminescence(PL) spectra. The results showed that the ZnO thin films with Au buffer layer is of high crystallinic qualities and is highly

c

-axis oriented. The prepared ZnO thin films on gold-plated quartz substrates at 500 ℃ are found to be compact and uniform

with better crystallinic qualities. A strong band edge emission in the PL spectra associated with the free exciton emission is observed at about 400 nm

while other emissions related to specific defects could be negligible compared with the intensive UV emission

which indicated that the ZnO thin films has low concentration of defects and high crystal qualities.

关键词

Keywords

references

Jason B Baxter, Wu Feng, Eray S Aydil. Growth mechanism and characterization of zinc oxide hexagonal columns [J]. Appl. Phys. Lett., 2003, 83(18):3797-3799.[2] Zu P, Tang Z K, Wong G K L, et al. Ultraviolet spontaneous and stimulated emissions from ZnO microcrystallite thin films at room temperature [J]. Sol. Stat. Commun., 1997, 103(8):459-463.[3] Vanheusden K, Seager C H, Warren W L, et al. Correlation between photoluminescence and oxygen vacancies in ZnO phosphors [J]. Phys. Stat. Sol.(b), 1996, 68(3):403-405.[4] Cui Junpeng, Duan Yao, Wang Xiaofeng, et al. ZnO film grown on Si substrate with an Au buffer layer [J]. Chin. J. Lumin.(发光学报)， 2008, 29(10):861-864 (in Chinese).[5] Vispute R D, Talyansky V, Choopun S, et al. Heteroepitaxy of ZnO on GaN and its implications for fabrication of hybrid optoelectronic devices [J]. Appl. Phys. Lett., 1998, 73(3):349-351.[6] Lan Zhenli, Zhang Xiqing, Yang Guangwu, et al. Structural and optical characterization of ZnO thin films grown by plasma-assisted molecular beam epitaxy [J]. Spectroscopy and Spectral Analysis (光谱学与光谱分析)， 2008, 28(2):253-255 (in Chinese).

0

浏览量

111

下载量

0

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

相关文章

掺杂富勒烯衍生物阻变存储器存储性质的调控研究

梯度组分缓冲层诱导的单一立方相Mg_0.3Zn_0.7O薄膜外延生长

透明导电ZnO薄膜的电化学制备及性能研究

电沉积法制备ZnO纳米柱及其机制研究

利用MOCVD在r面蓝宝石上生长的 a面GaN中两步AlN缓冲层的优化

相关作者

李静玉

林青

章婷

邓朝勇

郑剑

张振中

王立昆

韩舜

相关机构

贵州大学大数据与信息工程学院

北京理工大学光电学院

东北师范大学先进光电功能材料研究中心

中国科学院大学

发光学及应用国家重点实验室中国科学院长春光学精密机械与物理研究所

AI问答

地址：长春市经济技术开发区东南湖大路3888号邮编：130033
联系电话：0431-86176862 Email：fgxbt@126.com
本系统由Light学术出版中心、北京北大方正电子有限公司共建吉ICP备11002662号-17 京公网安备11010802024621
本系统建议在Chrome、 IE9+ 以上版本浏览器阅读本站内容，360浏览器请切换至极速模式
Cookies帮助我们提供服务并提供个性化体验。使用本网站，即表示您同意我们使用Cookies

⁰