李乾利, 胡亚华, 马玉彬等. Lu<sub>2</sub>Si<sub>2</sub>O<sub>7</sub>∶Ce纳米晶的溶胶-凝胶法合成和闪烁性能[J]. 发光学报, 2020,41(4): 364-370
LI Qian-li, HU Ya-hua, MA Yu-bin etc. Sol-gel Synthesis and Scintillation Properties of Lu<sub>2</sub>Si<sub>2</sub>O<sub>7</sub>∶Ce Nanocrystalline[J]. Chinese Journal of Luminescence, 2020,41(4): 364-370
李乾利, 胡亚华, 马玉彬等. Lu<sub>2</sub>Si<sub>2</sub>O<sub>7</sub>∶Ce纳米晶的溶胶-凝胶法合成和闪烁性能[J]. 发光学报, 2020,41(4): 364-370 DOI: 10.3788/fgxb20204104.0364.
LI Qian-li, HU Ya-hua, MA Yu-bin etc. Sol-gel Synthesis and Scintillation Properties of Lu<sub>2</sub>Si<sub>2</sub>O<sub>7</sub>∶Ce Nanocrystalline[J]. Chinese Journal of Luminescence, 2020,41(4): 364-370 DOI: 10.3788/fgxb20204104.0364.
采用溶胶-凝胶法制备了Lu
2
Si
2
O
7
∶Ce纳米晶,利用X射线衍射(XRD)、扫描电镜(SEM)、荧光光谱仪、X射线激发发射谱仪对制备的Lu
2
Si
2
O
7
∶Ce纳米晶的晶相结构、微观形貌和光学性能进行了表征。结果表明,溶胶-凝胶法制备的Lu
2
Si
2
O
7
∶Ce前驱体在煅烧温度为1 000℃时开始晶化,晶粒尺寸随着煅烧温度的升高而变大,1 200℃煅烧2 h后的晶体颗粒均匀,分散性最优,平均晶粒尺寸约为28.9 nm,呈近球形;Lu
2
Si
2
O
7
∶Ce纳米晶的紫外吸收谱存在峰位分别为304 nm和350 nm两个吸收峰,源自于Ce
3+
离子的4f5d跃迁;光致发射谱和X射线激发发射谱都表现为典型的非对称双峰结构,归属于Ce
3+
离子的5d
1
2
F
5/2
和5d
1
2
F
7/2
跃迁,Ce
3+
离子的最佳掺杂浓度约为1%;荧光衰减时间约为37.2 ns,可满足高时间分辨X射线探测需要。
Cerium-doped lutetium pyrosilicate Lu
2
Si
2
O
7
∶Ce nanocrystalline was synthesized by the sol-gel method. The structure
morphologies and scintillation properties of Lu
2
Si
2
O
7
∶Ce nanocrystalline were characterized by X-ray diffractometer (XRD)
scanning electron microscope (SEM)
photoluminescence and X-ray excited luminescence. The results indicate that Lu
2
Si
2
O
7
∶Ce starts to crystallize at about 1 000 ℃ and the crystallite size increases with the increasing calcining temperature. Well dispersed
homogeneous and near-spherical Lu
2
Si
2
O
7
∶Ce powder with an average grain size about 28.9 nm was obtained after sintering at 1 200 ℃ for 2 h. The excitation spectrum consists of two intense broad bands at 304 nm and 350 nm
which are corresponding to the 4f5d transition of Ce
3+
ions. The emission peak under 350 nm and X-ray excitation both exhibit a typical asymmetric peak
which are attribute to 5d
1
2
F
5/2
and 5d
1
2
F
7/2
transition of the Ce
3+
ions. The optimized doping concentration of Ce
3+
ion is about 1%. The decay time of the as-prepared Lu
2
Si
2
O
7
∶Ce phosphor is about 37.2 ns
which can satisfy the requirement of the X-ray detection with high time resolution.
闪烁材料Lu2Si2O7∶Ce纳米晶溶胶-凝胶法荧光光谱X射线探测
scintillation materialsLu2Si2O7∶Ce nanocrystallinesol-gel methodphotoluminescenceX-ray detection
LUO Z P,MOCH J G,JOHNSON S S,et al.. A review on X-ray detection using nanomaterials [J]. Curr. Nanosci., 2017,13(4):364-372.
NIKL M,YOSHIKAWA A,VEDDA A,et al.. Development of novel scintillator crystals [J]. J. Cryst. Growth, 2006,292(2):416-421.
侯晴,陈建玉,齐红基,等. Yb∶YAG超快闪烁晶体研究进展与展望 [J]. 发光学报, 2016,37(11):1323-1331. HOU Q,CHEN J Y,QI H J,et al.. Research progress and prospect of Yb-doped YAG ultrafast scintillation crystal [J]. Chin. J. Lumin., 2016,37(11):1323-1331. (in Chinese)
HU Y S,QIN Z,MA Y,et al.. Characterization of fiber radiation dosimeters with different embedded scintillator materials for radiotherapy applications [J]. Sens. Actuators A:Phys., 2018,269:188-195.
严成锋,赵广军,杭寅,等. 稀土焦硅酸盐Re2Si2O7闪烁晶体的研究进展 [J]. 人工晶体学报, 2005,34(1):144-148. YAN C F,ZHAO G J,HANG Y,et al.. Reseach progress in inorganic scintillation crystal Re2Si5O7 [J]. J. Synth. Cryst., 2005,34(1):144-148. (in Chinese)
PIDOL L,VIANA B,KAHN-HARARI A,et al.. Scintillation and thermoluminescence properties of Lu2Si2O7∶Ce3+ crystals [J]. Nucl. Instrum. Methods Phys. Res. A, 2005,537(1-2):256-260.
FENG H,DING D Z,LI H Y,et al.. Cerium concentration and temperature dependence of the luminescence of Lu2Si2O7∶Ce scintillator [J]. J. Alloys Compd., 2011,509(9):3855-3858.
YAN C F,ZHAO G Z,HANG Y,et al.. Comparison of cerium-doped Lu2Si2O7 and Lu2SiO5 scintillators [J]. J. Cryst. Growth, 2005,281(2-4):411-415.
李焕英,秦来顺,姚冬敏,等. Lu2Si2O7∶Ce晶体的闪烁性能 [J]. 发光学报, 2006,27(5):729-734. LI H Y,QIN L S,YAO D M,et al.. Scintillation properties of Lu2Si2O7∶Ce crystal [J]. Chin. J. Lumin., 2006,27(5):729-734. (in Chinese)
YAN C F,ZHAO G Z,HANG Y,et al.. Czochralski growth and crystal structure of cerium-doped Lu2Si2O7 scintillator [J]. Mater. Lett. Growth, 2006,60(16):1960-1963.
LU Q,LIU Q,ZHUANG J D,et al.. Ce3+-doped Lu2Si2O7 luminescent fibers derived from electrospinning:facile preparation and flexible fiber molding [J]. J. Mater. Sci., 2013,48(24):8471-8482.
PIDOL L,KAHN-HARARI A,VIANA B,et al.. Czochralski growth and physical properties of cerium-doped lutetium pyrosilicate scintillators Ce3+∶Lu2Si2O7 [J]. J. Cryst. Growth, 2005,275(1-2):e899-e904.
EGODAWATTE S,ZHANG E,POSEY T J,et al.. Synthesis of scintillating Ce3+-doped Lu2Si2O7 nanoparticles using the salt-supported high temperature (SSHT) method:solid state chemistry at the nanoscale [J]. ACS Appl. Nano Mater., 2019,2(4):1857-1865.
HORIAI T,KUROSAWA S,MURAKAMI R,et al.. Crystal growth and optical properties of Gd admixed Ce-doepd Lu2Si2O7 single crystals [J]. J. Cryst. Growth, 2017,468:391-394.
LI Y,YOU B G,ZHANG W P,et al.. Luminescent properties of -Lu2Si2O7∶RE3+(RE=Ce,Tb) nanoparticles by sol-gel method [J]. J. Rare Earths, 2008,26(3):455-458.
FAN L C,XU J,SHI Y,et al.. Lower temperature synthesis of cerium-doped polycrystalline lutetium pyrosilicate powders by a novel sol-gel processing [J]. Sci. China Technol. Sci., 2014,57(8):1610-1615.
王林香,祝恒江,尹民. Lu2O3∶Eu3+纳米粉末及透明陶瓷的制备及其发光性能 [J]. 发光学报, 2011,32(9):913-919. WANG L X,ZHU H J,YIN M. Fabrication and luminescent properties of Eu3+-doped Lu2O3 nanopowders and transparent ceramics [J]. Chin. J. Lumin., 2011,32(9):913-919. (in Chinese)
TRIPATHI H S,SARIN V K. Synthesis and densification of lutetium pyrosilicate from lutetia and silica [J]. Mater. Res. Bull., 2007,42(2):197-202.
SOKOLNICKI J,GUZIK M. Synthesis and photoluminescence of nanocrystalline lutetium pyrosilicate doped with Ce3+[J]. Opt. Mater., 2009,31(6):826-830.
NEDELEC J C. Sol-gel processing of nanostructured inorganic scintillating materials [J]. J. Nanomater., 2007,2007(1):9-1-8.
JAYASEELAN D D,UENO S,OHJI T,et al.. Sol-gel synthesis and coating of nanocrystalline Lu2Si2O7 on Si3N4 substrate [J]. Mater. Chem. Phys., 2004,84(1):192-195.
NIZNANSKY D,BEGNAMINI A,VEJPRAVOVA-POLTIEROVA J V,et al.. Doped Lutetium silicates scintillators prepared by sol-gel method. The effect of stoichiometry on phase relations and luminescent properties [J]. IOP Conf. Ser.:Mater. Sci. Eng., 2011,18(10):102020-1-4.
PILANIA G,YADAV S K,NIKL M,et al.. Role of multiple charge states of Ce in the scintillation of ABO3 perovskites [J]. Phys. Rev. Appl., 2018,10(2):024026-1-17.
PEJCHAL J,BARTA J,BABIN V,et al.. Influence of Mg-codoping,non-stoichiometry and Ga-admixture on LuAG∶Ce scintillation properties [J]. Opt. Mater., 2018,86:213-232.
梁宏斌,田梓峰,钟玖平,等. Ce3+离子激活的(氟)磷酸盐基质发光材料的光谱特性 [J]. 发光学报, 2011,32(5):411-416. LIANG H B,TIAN Z F,ZHONG J P,et al.. Luminescence of Ce3+ activated (fluoro-) phosphates under VUV-UV and X-ray excitation [J]. Chin. J. Lumin., 2011,32(5):411-416. (in Chinese)
任国浩,李焕英,陆晟,等. 焦硅酸镥(Lu2Si2O7∶Ce)闪烁晶体的生长与发光性能研究 [J]. 人工晶体学报, 2007,36(5):967-970. REN G H,LI H Y,LU S,et al.. Growth and luminescence properties of lutetium pyrosilicate (Lu2Si2O7∶Ce) scintillation crystals [J]. J. Synth. Cryst., 2007,36(5):967-970. (in Chinese)
0
浏览量
94
下载量
0
CSCD
关联资源
相关文章
相关作者
相关机构