艾哲, 倪帅帅, 张亚非. 基于CuInS<sub>2</sub>/ZnS核壳结构量子点的高光效暖白光LED[J]. 发光学报, 2015,36(11): 1282-1288
AI Zhe, NI Shuai-shuai, ZHANG Ya-fei. Warm White LED with High Luminous Efficiency Based on CuInS<sub>2</sub>/ZnS Core/Shell Quantum Dots[J]. Chinese Journal of Luminescence, 2015,36(11): 1282-1288
艾哲, 倪帅帅, 张亚非. 基于CuInS<sub>2</sub>/ZnS核壳结构量子点的高光效暖白光LED[J]. 发光学报, 2015,36(11): 1282-1288 DOI: 10.3788/fgxb20153611.1282.
AI Zhe, NI Shuai-shuai, ZHANG Ya-fei. Warm White LED with High Luminous Efficiency Based on CuInS<sub>2</sub>/ZnS Core/Shell Quantum Dots[J]. Chinese Journal of Luminescence, 2015,36(11): 1282-1288 DOI: 10.3788/fgxb20153611.1282.
采用逐步热注射法合成了用于白光LED的CuInS
2
/ZnS(CIS/ZnS)核壳结构量子点.通过调整Cu/In的比率
在CuInS
2
(CIS)量子点的基础上
合成了发射波长在570~650 nm之间可调的CIS/ZnS量子点.与CIS量子点的低量子产率相比
具有核壳结构的CIS/ZnS量子点的量子产率达到了78%.通过在黄光荧光粉YAG :Ce
3+
表面旋涂CIS/ZnS量子点的方式制备了暖白光LED器件.在工作电流为10 mA时
暖白光LED的发光效率达到了244.58 lm/W.由于CIS/ZnS量子点的加入
所制备的白光LED器件的显色指数达到86.7且发光颜色向暖色调发生了转移
相应的色坐标为(0.340 6
0.369 0).
A stepwise hot-injection method was proposed to synthesize CuInS
2
/ZnS (CIS/ZnS) core/shell quantum dots. Based on CIS quantum dots
the emission bands of the prepared CIS/ZnS quantum dots can be tuned from 570 to 650 nm by varying Cu/In ratio. Compared to the low quantum yields of CIS quantum dots
the quantum yields of CIS/ZnS core/shell quantum dots can reach 78%. The white LEDs with warm tone were successfully obtained
via
spin-coating CIS/ZnS quantum dots on the yellow phosphor YAG :Ce
3+
. The experimental results indicate that the white LEDs possess high luminous efficiency of 244.58 lm/W under 10 mA current density. As a result of joining CIS/ZnS quantum dots
the prepared white LEDs display higher color rendering index (CRI) of about 82.7 and warm white light with a correlated CIE parameters of (0.340 6
0.369 0).
CuInS2/ZnS核壳结构量子点可调暖白光
CuInS2/ZnScore/shell quantum dotstunablewarm white light
Arzu C, Ren L F, Wei N J, et al. Flexible quantum dot-PVA composites for white LEDs [J]. J. Mater. Chem. C, 2015, 3(2):257-264.
Talapin D V, Lee J S, Kovalenko M V, et al. Prospects of colloidal nanocrystals for electronic and optoelectronic applications [J]. Chem. Rev., 2010, 110(1):389-458.
Kamat P V. Quantum dot solar cells. Semiconductor nanocrystals as light harvesters [J]. J. Phys. Chem. C, 2008, 112(48):18737-18753.
Smith A M, Duan H W, Mohs A M, et al. Bioconjugated quantum dots for in vivo molecular and cellular imaging [J]. Adv. Drug Deliv. Rev., 2008, 60(11):1226-1240.
Xie R, Rutherford M, Peng X G. Formation of high-quality Ⅰ-Ⅲ-Ⅵ semiconductor nanocrystals by tuning relative reactivity of cationic precursors [J]. J. Am. Chem. Soc., 2009, 131(15):5691-5697.
Zhong H Z, Zhou Y, Ye M F, et al. Controlled synthesis and optical properties of colloidal ternary chalcogenide CuInS2 nanocrystals [J]. Chem. Mater., 2008, 20(20):6434-6443.
Li L, Daou T J, Texier I, et al. Highly luminescent CuInS2/ZnS core/shell nanocrystals: Cadmium-free quantum dots for in vivo imaging [J]. Chem. Mater., 2009, 21(12):2422-2429.
Li T L, Teng H. Solution synthesis of high-quality CuInS2 quantum dots as sensitizers for TiO2 photoelectrodes [J]. J. Mater. Chem., 2010, 20:3656-3664.
Nose K, Soma Y, Omata T, et al. Synthesis of ternary CuInS2 nanocrystals; phase determination by complex ligand species [J]. Chem. Mater., 2009, 21(13):2607-2613.
Woo S S, Heesun Y. Efficient white-light-emitting diodes fabricated from highly fluorescent copper indium slfide core/shell quantum dots [J]. Chem. Mater., 2012, 24(10):1961-1967.
Chen Y H, Zhang X, Zhou J, et al. Effect of red, green CdSe@ZnS quantum dots ratios on standard three-band white LED devices [J]. Chin. J. Lumin.(发光学报), 2014, 35(8):992-997 (in Chinese).
Wen J Z, Qing L, Wen Y J, et al. Color-tunable highly bright photoluminescence of cadmium-free cu-doped Zn-In-S nanocrystals and electroluminescence [J]. Chem. Mater., 2014, 26(2):1204-1212.
Chuang P H, Lin C C, Liu R S. Emission-tunable CuInS2/ZnS quantum dots: Structure, optical properties, and application in white light-emitting diodes with high color rendering index [J]. Appl. Mater. Interf., 2014, 6(17):15379-15387.
Uehara M, Watanabe K, Tajiri Y, et al. Synthesis of CuInS2 fluorescent nanocrystals and enhancement of fluorescence by controlling crystal defect [J]. J. Chem. Phys., 2008, 129(13):134709-1-6.
Kim Y K, Ahn S H, Chung K, et al. The photoluminescence of CuInS2 nanocrystals: Effect of non-stoichiometry and surface modification [J]. J. Mater. Chem., 2012, 22:1516-1520.
Chen B K, Zhong H Z, Zhang W Q, et al. Highly emissive and color-tunable CuInS2-based colloidal semiconductor nanocrystals: Off-stoichiometry effects and improved electroluminescence performance [J]. Adv. Funct. Mater., 2012, 22:2081-2088.
Dai M L, Ogawa S, Kameyama T, et al. Tunable photoluminescence from the visible to near-infrared wavelength region of nonstoichiometric AgInS2 nanoparticles [J]. J. Mater. Chem., 2012, 22:12851-12858.
Deng D W, Yu J S. Photoluminescence properties of citrate-stabilized water-soluble CdSe and CdSe/CdS quantum dots [J]. Chin. J. Inorg. Chem.(无机化学学报), 2008, 24(5):701-707 (in Chinese).
Qu L Z, Chen Z Q, Deng D W, et al. Oil-soluble CuInS2/ZnS quantum dots and water transfer using temperature-sensitive poly (N-isopropylacrylamide-co-aerylamide-co-octadecyl acrylatel) micelle [J]. Chin. J. Inorg. Chem (无机化学学报), 2013, 29(7):1361-1368 (in Chinese).
0
浏览量
75
下载量
3
CSCD
关联资源
相关文章
相关作者
相关机构