李君飞, 饶海波, 侯 斌, 等. 基于粉浆法提高功率型白光LEDs的提取效率[J]. 发光学报, 2009,30(1):19-24.
LI Jun-fei, RAO Hai-bo, HOU Bin, et al. Investigation on Improving the Extraction Efficiency of Power White LEDs with Slurry Method[J]. Chinese Journal of Luminescence, 2009,30(1):19-24.
讨论了基于水溶性感光胶的荧光粉的涂层技术,利用粉浆法,在蓝光LED芯片的表面获得了荧光粉平面涂层。证实了得到的白光LED的光提取效率与粉浆中各成份的浓度和相应的比例有关,并在实验的基础上,采用了一些切实切可行的措施来增加器件的光提取效率。得到的白光LED在700 mA加速老化168 h后,其光能量为初始时的95.95%。
Slurry method based on a phosphor suspension in a water-soluble photoresist was discussed. A conformal-coating phosphor layer was deposited on the surface of LEDs. The luminous performance of power white LEDs was found to be mainly depending on the concentration and ratio of ingredients in slurry and the structure of coating layer. In this paper, the parameters were investigated and some advices, which were suggested to improve the performance, were proven to be effective in our experiment. The aging testing of LEDs with this slurry method showed that the luminous flux was 95.95% of that of the beginning after the LED was lightened for 168 h at 700 mA.
white LEDsslurryextraction efficiencypackaging
. Nakamura S, Mukai T, Sench M. Candela-class high-brightness InGaN/AlGaN double-heterostructure blue-light-emitting diodes [J]. Appl. Phys. Lett., 1994, 64 (13):1687-1689.
. Murakami K, Taguchi T, Yoshino M. White illumination characteristics of ZnS-based phosphor materials excited by InGaN-based ultraviolet light-emitling diode [J]. SPIE, 2000, 4079 :112-119.
. Uchida Y, Setomoto T, Taguchi T, et al. Characteristics of light-efficiency InGaN-based white LED lighting [J]. SPIE, 2000, 4079 :120-126.
. Yam F K, Hassan Z. Innovative advances in LED technology [J]. Microelectronics Journal, 2005, 36 (2):129-137.
. Zhang Guoyou, Zhao Xiaoxia, Meng Qingyu, et al. Preparatiion and properties of red emitting phosphor Gd2Mo3O9 ∶ Eu3+ for white LEDs [J]. Chin. J. Lumin. (发光学报), 2007, 28 (1):57-61 (in Chinese).
. Liu Xingren. Phosphors for white LED solid state lightting [J]. Chin. J. Lumin. (发光学报), 2007, 28 (3):291-301 (in Chinese).
. Yang Yi, Jin Shangzhang, Shen Changyu, et al. Spectral properties of alkaline earth composite sillicate phosphors for white-LED [J]. Chin. J. Lumin. (发光学报), 2008, 29 (5):800-804 (in Chinese).
. Fang Fubo, Wang Yachao, Song Daihui, et al. Spectroscopic analysis of white LED attenuation [J]. Chin. J. Lumin. (发光学报), 2008, 29 (2):353-357 (in Chinese).
. Xu Guofang, Rao Haibo, Yu Xinmei, et al. Improvement of optical uniformity of white LEDs [J]. Chin. J. Lumin. (发光学报), 2008, 29 (3):707-712 (in Chinese).
. Steranka F M, Bhat J, Collins D, et al. High power LEDs-technology status and market applications [J]. Phys. Stat. Sol. (a), 2002, 194 (2):380-388.
. Yu X M, Rao H B, Hu Y, et al. A phosphor coating process for white LEDs application . ISTC,Packaging and Assembly, Shanghai: China:Ming Yang, 2007, 864-870
. William D Collins, Wayne L Snyder, Daniel A Steigerwald. Producing self-aligned and self-exposed photoresist pattern on light emitting devices. US: 6756186B2 . 2004-06-29.
. Yum Jun-Ho, Seo Soo-Yeon, Lee Seonghoon, et al. Comparison of Y3A15O12 ∶ Ce0.05 phosphor coating methods for white light emitting diode on gallium nitride [J]. SPIE, 2001, 4445 :60-69.
. Keith Y. Sasaki, Jan B Talbot. Deposition of powder phosphors for information displays [J]. Adv. Mater. , 1999, 11 (2):91-105.
. Xu J, Zhang Q, Deng P Z, et al. Optical absorption spectrum of Cr3+ and Cr4+ in Sr3Ga2Ge4O14 garnet crystals [J]. Acta Optica Sinica (光学学报), 1995, 5 (7):871-873 (in Chinese).