溶胶凝胶法制备Zn1-xFexO稀磁半导体

蒋婧思; 侯延冰; 唐爱伟; 滕枫

doi:null

您当前的位置：

首页 >

文章列表页 >

溶胶凝胶法制备Zn_1-xFe_xO稀磁半导体

第八届全国发光学学术会议研究论文 | 更新时间：2020-08-11

- 溶胶凝胶法制备Zn_1-xFe_xO稀磁半导体
- Zn_1-xFe_xO Diluted Magnetic Semiconductor Fabricated with Sol-gel Method
- 发光学报 2008年29卷第1期页码：149-151
- 作者机构：
  
  北京交通大学光电子技术研究所北京,100044
- 作者简介：
- 基金信息：
  
  教育部跨世纪人才基金();教育部重点项目(105041)();自然基金(90401006,10434030和90301004)();“973”计划(2003CB3147
- DOI：
  中图分类号： O472.5
- 收稿日期：2007-08-25，
  
  修回日期：2007-11-24，
  
  纸质出版日期：2008-01-20
- 稿件说明：
移动端阅览
蒋婧思, 侯延冰, 唐爱伟, 滕枫. 溶胶凝胶法制备Zn1-xFexO稀磁半导体[J]. 发光学报, 2008,29(1): 149-151

JIANG Jing-si, HOU Yan-bing, TANG Ai-wei, TENG Feng. Zn1-xFexO Diluted Magnetic Semiconductor Fabricated with Sol-gel Method[J]. Chinese Journal of Luminescence, 2008,29(1): 149-151
蒋婧思, 侯延冰, 唐爱伟, 滕枫. 溶胶凝胶法制备Zn1-xFexO稀磁半导体[J]. 发光学报, 2008,29(1): 149-151 DOI：

JIANG Jing-si, HOU Yan-bing, TANG Ai-wei, TENG Feng. Zn1-xFexO Diluted Magnetic Semiconductor Fabricated with Sol-gel Method[J]. Chinese Journal of Luminescence, 2008,29(1): 149-151 DOI：

摘要

使用溶胶-凝胶法

制备了Fe掺杂的ZnO粉末衡磁半导体材料。通过X射线衍射对样品的晶格结构进行了分析

发现衍射峰的峰位随着Fe掺杂量出现偏移。当掺杂浓度低于6.66%时

Fe较好地替代了Zn的晶格位置

当掺杂浓度达到6.66%时出现杂相峰。使用超导量子干涉仪对所制备的磁性材料进行表征

得到了材料磁化率随温度变化关系曲线

并观察到明显的低温磁滞现象。对其磁性来源进行了分析。

Abstract

A Zn

1-x

O diluted magnetic semiconductor was synthesized with Sol-Gel method. Combining zinc acetate dehydrate with FeCl

in a certain percentage and dissolve in ethanol

using lactic acid as stabilizer

transparent sol can be synthesized after three hours reaction. Powder sample can be formed through the process of drying by distillation

elimination of organics and heat processing. Crystal structure of Zn

1-x

O sample was analyzed with X-ray diffraction

and only ZnO diffraction peaks can be found with doping concentration lower than 6.66%. An increase in the hexagonal lattice parameters of ZnO is observed on increasing the Fe concentration.

M-T

curve of the powder material was measured with Superconducting Magnet System

the magnetic loop can be observed at the temperature of 10 K.

关键词

Keywords

references

浏览量

103

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

(Cu,Al)掺杂ZnO薄膜表面处缺陷的拉曼光谱研究

高增益ZnO肖特基紫外光电探测器光响应特性

利用离子激发发光研究低温条件下ZnO发光行为

生长温度对MOCVD外延ZnO纳米结构的影响

稀土离子掺杂LaAlO₃:RE³⁺(RE=Eu,Tb,Sm,Tm)荧光粉的发光性能