p型MgxZn1-xO薄膜材料的制备与光学特性

董鑫; 赵旺; 张宝林; 李香萍; 杜国同

doi:null

您当前的位置：

首页 >

文章列表页 >

p型Mg_xZn_1-xO薄膜材料的制备与光学特性

第八届全国发光学学术会议研究论文 | 更新时间：2020-08-11

- p型Mg_xZn_1-xO薄膜材料的制备与光学特性
- Study on Optical Properties of p-type MgZnO Fabricated by MOCVD
- 发光学报 2008年29卷第1期页码：129-132
- 作者机构：
  
  1. 大连理工大学, 物理与光电工程学院,辽宁大连,116033
  2. 吉林大学电子科学与工程学院, 集成光电子国家重点实验室,吉林长春,130012
- 作者简介：
- 基金信息：
  
  国家自然科学基金资助项目(60576054,50532080)()
- DOI：
  中图分类号： O472.3;O482.31
- 收稿日期：2007-08-25，
  
  修回日期：2007-11-24，
  
  纸质出版日期：2008-01-20
- 稿件说明：
移动端阅览
董鑫, 赵旺, 张宝林, 李香萍, 杜国同. p型MgxZn1-xO薄膜材料的制备与光学特性[J]. 发光学报, 2008,29(1): 129-132

DONG Xin, ZHAO Wang, ZHANG Bao-lin, LI Xiang-ping, DU Gou-tong. Study on Optical Properties of p-type MgZnO Fabricated by MOCVD[J]. Chinese Journal of Luminescence, 2008,29(1): 129-132
董鑫, 赵旺, 张宝林, 李香萍, 杜国同. p型MgxZn1-xO薄膜材料的制备与光学特性[J]. 发光学报, 2008,29(1): 129-132 DOI：

DONG Xin, ZHAO Wang, ZHANG Bao-lin, LI Xiang-ping, DU Gou-tong. Study on Optical Properties of p-type MgZnO Fabricated by MOCVD[J]. Chinese Journal of Luminescence, 2008,29(1): 129-132 DOI：

摘要

通过金属有机化学汽相沉积(MOCVD)法在GaAs衬底上生长出了Mg

1-x

O薄膜

通过氧气气氛下的高温退火使得衬底中的As原子通过扩散作用进入薄膜形成受主

得到p型的Mg

1-x

O薄膜。退火前后XPS谱中As(3d)峰的对比表明

1-x

O薄膜中存在As。电学测试结果表明:退火对样品的电阻率和载流子浓度的影响很大。这是长时间的氧气退火使得氧空位数目明显减少

从而使Zn—O键数量显著增加造成的。在样品的X射线衍射(XRD)谱中

p型样品的(002)衍射峰明显弱于n型样品。而在二者的光致发光(PL)谱中

都存在着很强的近带边发射(NBE)峰和较弱的深能级发射(DLE)峰

p型样品的NBE峰明显较弱而DLE峰却很强。这些现象是由于As原子的扩散

使薄膜中产生了新的缺陷能级

导致能级间的激子复合更加复杂。稳定的p型Mg

1-x

O薄膜的获得为制备Mg

1-x

O同质结和发光二极管奠定了基础。

Abstract

p-type Mg

1-x

O film was grown on semi-insulating GaAs substrate by metal-organic chemical vapor deposition. The arsenic atoms

which acted as the acceptors in the film

were diffused from the substrates when the film was annealed in oxygen ambient at 700℃. And the cause of formation about p-type film was also discussed. The measurements

such as the XPS

HALL

XRD and PL were carried out. The existence of As in the film was proved by XPS. The resistivities and carrier concentrations of the film were measured by HALL effect measurement and the effect of anneal in the oxygen on them were discussed. The (002) peak in the XRD pattern and the NBE peak in the PL spectra of n-MgZnO were both stronger than that of p-MgZnO. The reason was believed that the new defects were introduced by As diffusion.

关键词

Keywords

references

浏览量

124

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

射频等离子硫钝化GaAs(100)的表面特性

碳硅共掺杂p型AlN的光电性能研究

AlN插入层对a-AlGaN的外延生长的影响

衬底温度对ZnO薄膜的结构和光学特性的影响

Ca₂MgSi₂O₇ :Eu²⁺绿色发光粉的低温合成及光致发光