(Ba, Mg, Sr)O&#183;nAl2O3:Mn2+的合成及发光性质研究

沈雷军; 张忠义; 韩莉; 周永勃; 刘翠兰; 陶冶; 巨新

doi:null

您当前的位置：

首页 >

文章列表页 >

(Ba, Mg, Sr)O·nAl₂O₃:Mn²⁺的合成及发光性质研究

研究论文 | 更新时间：2020-08-11

- (Ba, Mg, Sr)O·nAl₂O₃:Mn²⁺的合成及发光性质研究
- Synthesis and Properties of (Ba, Mg, Sr)O·nAl₂O₃:Mn²⁺ Phosphors
- 发光学报 2003年24卷第2期页码：189-193
- 作者机构：
  
  1. 包头稀土研究院,内蒙古包头,014010
  2. 中国科学院高能物理研究所, 同步辐射实验室, 北京, 100039
- 作者简介：
- 基金信息：
  
  孵化基金资助项目(00318)()
- DOI：
  中图分类号： O482.31
- 收稿日期：2002-09-11，
  
  修回日期：2002-12-06，
  
  纸质出版日期：2003-03-20
- 稿件说明：
移动端阅览
沈雷军, 张忠义, 韩莉, 周永勃, 刘翠兰, 陶冶, 巨新. (Ba, Mg, Sr)O·nAl2O3:Mn2+的合成及发光性质研究[J]. 发光学报, 2003,24(2): 189-193

SHEN Lei-jun, ZHANG Zhong-yi, HAN Li, ZHOU Yong-bo, LIU Chui-lan, TAO Ye, JU Xin. Synthesis and Properties of (Ba, Mg, Sr)O·nAl2O3:Mn2+ Phosphors[J]. Chinese Journal of Luminescence, 2003,24(2): 189-193
沈雷军, 张忠义, 韩莉, 周永勃, 刘翠兰, 陶冶, 巨新. (Ba, Mg, Sr)O·nAl2O3:Mn2+的合成及发光性质研究[J]. 发光学报, 2003,24(2): 189-193 DOI：

SHEN Lei-jun, ZHANG Zhong-yi, HAN Li, ZHOU Yong-bo, LIU Chui-lan, TAO Ye, JU Xin. Synthesis and Properties of (Ba, Mg, Sr)O·nAl2O3:Mn2+ Phosphors[J]. Chinese Journal of Luminescence, 2003,24(2): 189-193 DOI：

摘要

用高温固相反应合成了Ba

0.04

0.16

0.8

O·

:Mn

0.07

(

=4.1

4.2…4.9)和Ba

0.1

0.8

O·

:Mn

0.07

(

=4.1

4.2…4.9)铝酸盐体系发光材料。X射线衍射呈单相

说明生成了完全互溶的连续固溶体。经检测发现Mg

的引入有效地优化了发光基质

使Mn

在真空紫外激发下的发射明显增强。在Ba

0.04

0.16

0.8

O·

:Mn

0.07

体系中

在一定范围内改变Al

含量(

值)可适当调整激发光谱峰位;适当调整Al

和Mn

的含量比可以改变体系的发光强度

以满足等离子平板显示(PDP)技术的需求。

Abstract

The samples in Ba

0.04

0.16

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9)and Ba

0.1

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9) were synthesized by solid-state reaction. According to X-ray diffractions

the structure of the samples were single-phase and formed solids. The excitation spectra of Ba

0.04

0.16

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9) and Ba

0.1

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9) were located at the scope of 100～300nm

and composed of tw o continuous zones:the first one originated from the host absorption about 170nm

the second one originated from the absorption of the transition 3d

→3d

of Mn

around 190～200nm.The absorption more than 200nm was very weak.It is said th at the absorption of VUV was very strong

and the absorption of UV was weak in the system of Ba

0.04

0.16

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9)and Ba

0.1

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9). The host absorption was very strong

the emission was almost invisibility

and the Mn

emission was very strong that the energy transfer from the host to Mn

can be observed.In the system of Ba

0.04

0.16

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9)

when the n increased from 4.1 to 4.9 that the emission sp ectra were changed obviously.At first

the peak was moved to red as the

=4.1～4.5. The peak moved to 178nm when then equaled 4.5. The peak was at 170nm as

=4.6～4.9.In the system of Ba

0.1

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9)

was taken the place of Mn

and come in to the center of tetrahedron in lattice.Of course

the brightness was reduce das then was increased.When the value of n and content of Mn

were changed in a scope

a high efficiency green luminescent material of Ba

0.04

0.16

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9)and Ba

0.1

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9) would be obtained. The luminescent material in the system of Ba

0.04

0.16

0.8

O·

:Mn

0.07

and BaMg

0.1

0.8

O·

:Mn

0.07

(

=4.1

4.2...4.9) will be used in PDPs in the future.

关键词

Keywords

references

浏览量

105

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

基质组成对Eu,Dy共掺杂铝酸锶发光性能的影响

NaGdMgTeO₆∶Eu³⁺荧光粉的光致发光及其多功能应用

CsFAMA混合阳离子钙钛矿的带尾态发光和热无序度分析

K₃La（PO₄）₂基质中Tb³⁺的发光和能量传递

近紫外基白光LEDs用KYBaSi₂O₇∶Bi³⁺蓝色荧光粉发光特性

(Ba, Mg, Sr)O·nAl2O3:Mn2+的合成及发光性质研究

Synthesis and Properties of (Ba, Mg, Sr)O·nAl2O3:Mn2+ Phosphors

DOI：

摘要

Abstract

关键词

Keywords

references

(Ba, Mg, Sr)O·nAl₂O₃:Mn²⁺的合成及发光性质研究

Synthesis and Properties of (Ba, Mg, Sr)O·nAl₂O₃:Mn²⁺ Phosphors