Prepared Photocatalytic of Spinel-type ZnAl2O4 Using AAO as A Template on Si Substrate

GAO Bo; ZHANG Hai-ming; ZHU Yan-jun; LI Qin; LI Jing

doi:null

您当前的位置：

首页 >

文章列表页 >

Prepared Photocatalytic of Spinel-type ZnAl₂O₄ Using AAO as A Template on Si Substrate

paper | 更新时间：2020-08-12

- Prepared Photocatalytic of Spinel-type ZnAl₂O₄ Using AAO as A Template on Si Substrate
- Chinese Journal of Luminescence Vol. 32, Issue 12, Pages: 1243-1246(2011)
- 作者机构：
  
  天津工业大学理学院天津,300160
- 作者简介：
- 基金信息：
- DOI：
  CLC： O643.36
- Received：14 June 2011，
  
  Revised：22 October 2011，
  
  Published Online：22 December 2011，
  
  Published：22 December 2011
- 稿件说明：
移动端阅览
高波, 张海明, 朱彦君, 李芹, 李菁. Si基AAO模板法制备尖晶石型ZnAl2O4纳米结构[J]. 发光学报, 2011,32(12): 1243-1246

GAO Bo, ZHANG Hai-ming, ZHU Yan-jun, LI Qin, LI Jing. Prepared Photocatalytic of Spinel-type ZnAl2O4 Using AAO as A Template on Si Substrate[J]. Chinese Journal of Luminescence, 2011,32(12): 1243-1246
高波, 张海明, 朱彦君, 李芹, 李菁. Si基AAO模板法制备尖晶石型ZnAl2O4纳米结构[J]. 发光学报, 2011,32(12): 1243-1246 DOI：

GAO Bo, ZHANG Hai-ming, ZHU Yan-jun, LI Qin, LI Jing. Prepared Photocatalytic of Spinel-type ZnAl2O4 Using AAO as A Template on Si Substrate[J]. Chinese Journal of Luminescence, 2011,32(12): 1243-1246 DOI：

摘要

以Si基AAO为模板

以Zn和C粉作蒸发源

通过化学气相沉积法

在不同的温度下反应得到了不同的ZnAl

纳米结构。对样品的形貌和成分结构进行了分析。扫描电镜结果显示

在800 ℃获得的ZnAl

样品表面仍保留着AAO模板的孔洞结构。而XRD结果表明

在700

800

900 ℃下获得的样品都出现了ZnAl

衍射峰

说明ZnAl

已经成功制备。结合SEM图和XRD图可以看出

800 ℃是制备尖晶石型光催化ZnAl

纳米结构的最合适温度。

Abstract

ZnAl

composite structure was fabricated using Zn and C powers by CVD method at different temperature. Structure and optical properties of the composite structure were investigated using scanning electron microscopy (SEM) and X-ray diffraction (XRD). SEM results indicated that the sample of ZnAl

structure prepared at 800 ℃ remained the regular pore structure of AAO template. The XRD patterns demonstrated that the diffraction peaks of the ZnAl

appeared at the reaction temperature of 700

800

900 ℃. That indicated the ZnAl

structures were obtained successfully. The optimum temperature for CVD method fabricated ZnAl

nanostructure was 800 ℃ by the SEM and XRD results.

关键词

Keywords

references

Fijishima A, Honda K. Electrochemical photolysis of water at a semiconductor electrode [J]. Nature, 1972, 238 (5358):37-38.[2] Linsebigler A L, Lu G, Yates J T. Photocatalysis on TiO2 surfaces: Principles, mechanisms, and selected results [J]. Chem. Rev., 1995, 95 (3):735-758.[3] Shen Junquan. Photocatalyst and its applications [J]. Advanced ceramics (现代技术陶瓷), 1998, 19 (1):32-38 (in Chinese).[4] Wang Z X, Ding S W, Zhang M H. Synthesis, structure and photocatalysis of nano-TiO2 mixed crystals [J]. Chin, J. Inorganic Chem.(无机化学学报), 2005, 21 (3):437-440 (in Chinese).[5] Mu Bailin, Hou Tianyi, Huo Lijuan, et al. Photocatalytic activity of ZnO/SnO2 coupled photocatalysts loaded on natural zeolite [J]. J. Chin. Ceramic Society (硅酸盐学报), 2005, 33 (11):1366-1370(in Chinese).[6] Clemens B, Lou Y, Chen X, Enhanced nitrogen doping in TiO2 nanoparticles [J]. Nano Lett., 2003, 3 (8):1049-1051.[7] Xie B, Wu Y, Qian Y T, et al. Shape-controlled synthesis of BaWO4 crystals under different surfactants [J]. J. Crystal Growth, 2002, 235 (1-4):283-286.[8] Petrov E P, Cichos F, Zenkevich E, et al. Tune resolved photoluminescence anisotropy of CdSe/ZnS nanoparticles in toluene at 300 K [J].Chem. Phys. Lett., 2005, 402 (1-3):233-238.[9] Lee S, Kim J, Lee C H, et al. Analysis of CaSO4 scale formation mechanism in various nanofiltration modules [J]. J. Membrane Science, 1999, 163 (1):63-74.[10] Ma S M, Wu B, Jiang X F, et al. PdCl2-catalyzed efficient transformation of propargylic amines to (E)--chloroalkylidene--lactams [J]. Journal of Organic Chemistry, 2005, 36 (34):2588-2593.[11] Xu T, Xie C S. Application of nano-materials in area of coationgs [J]. Chemical Industry and Engineering Progress, 2001, 20 (1):28-30.[12] Chen Ting, Zheng Hhuidan, Wang Pin, et al. Progress of perovskite photocatalysts in synthesis, modification doping and loading technique [J]. Chemical Engineer, 2008, 22 (8):17-20.[13] Li Zhe, Xu Pucha, Xue Limei. Preparation and photocatalytic reduction properties of visible light-driven spinel nano-particles [J]. Industrial Catalysis, 2010, 18 (6):19-22.[14] Yazdanbakhsh M, Khosravi I, Goharshadi E K, et al. Fabrication of nanospinel ZnCr2O4 using sol-gel method and its application on removal of azo dye from aqueous solution [J]. J. Hazard Mater., 2010, 184 (1-3):684-689.[15] Sampath S K, Cordaro J F, Ceram J A. Optical properties of zinc aluminate, zinc gallate, and zinc aluminogallate spinels [J]. J. American Ceramic Society, 1998, 81 (3):649-654.[16] Mathur S V, Mass M, Shen H, et al. Single-source sol-gel synthesis of nanocrystalline ZnAl2O4: Structural and optical properties [J]. J. American Ceramic Society, 2001, 84 (9):1921-1928.[17] Qin L, Jones G, Shen T. The growth of ordered ZnAl2O4 nanostructures using AAO as a reactive template [J]. Materials Letters, 2010, 64 (24):2685-2687.

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Performance of A Single Phosphorus-doped β-Ga₂O₃ Microwire Solar-blind Ultraviolet Photodetector

CVD Synthesis of Doped BN_x-graphene Hybrid Nanomaterials: Structure and Photoluminescence Properties

Controllable Synthesis of High Quality Monolayer WS₂ with Large Size on Sapphire Substrate by Chemical Vapor Deposition

Effects of Catalyst on Structures and Photoluminescence Properties of Graphene-like Nanoflakes

Synthesis and Photoluminescence Properties of Zinc Oxide Nanostructures

Related Author

Hong-wei LIANG

Wei LIU

Shuo LIANG

Chong GAO

Zeng-jie DONG

Jin-zhu XIE

Qiu-ju FENG

WANG Bi-ben

Related Institution

School of Physics and Electronic Technology, Liaoning Normal University

School of Microelectronics, Dalian University of Technology

College of Mathematics and Physics, Huaiyin Institute of Technology

College of Mechanical Engineering, Chongqing University of Technology

College of Chemistry and Chemical Engineering, Chongqing University of Technology

AI问答

Address：No.3888 Dong Nanhu Road, Changchun, Jilin, China Postal code：130033
Tel：0431-86176862 Email：fgxbt@126.com
Technical support is provided by Beijing Founder electronics co., LTD 吉ICP备11002662号-17 京公网安备11010802024621
It is recommended to read the content of this site in Chrome&IE9+. Please switch to extreme mode in browser 360.
Cookies We use cookies to help provide and enhance our service and tailor content. By continuing, you agree to the use of cookies.

⁰